Alkyl sulfonates of polyvinyl alcohol as viscosifiers in saline solutions

ABSTRACT

There are provided alkyl sulfonate salts derived from polyvinyl alcohols which are viscosifiers, e.g., for enhanced oil recovery fluids and for use in drilling fluids.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of parent U.S. application Ser. No. 391,214, filed June 23, 1982, in the name of Kirk D. Schmitt.

This application is further related to U.S. application Ser. No. 413,574, filed Aug. 31, 1982, in the name of Kirk D. Schmitt, which relates, inter alia, to pyrrolidinium methane sulfonates of polyvinyl alcohol which are viscosifiers, e.g., for use in enhanced oil recovery fluids and for use in drilling fluids.

The disclosures of the above-mentioned applications are expressly incorporated herein by reference.

BACKGROUND OF THE INVENTION

The present invention relates to alkyl sulfonate salts derived from polyvinyl alcohols which are viscosifiers, e.g., for enhanced oil recovery fluids and for use in drilling fluids.

In the recovery of oil from oil-bearing reservoirs, it usually is possible to recover only minor portions of the original oil in place by the so-called primary recovery methods which utilize only the natural forces present in the reservoir. Thus a variety of supplemental recovery techniques have been employed in order to increase the recovery of oil from subterranean reservoirs. The most widely used supplemental recovery technique is waterflooding which involves the injection of water into an oil-bearing reservoir. As the water moves through the reservoir, it acts to displace oil therein to a production system composed of one or more wells through which the oil is recovered.

One difficulty often encountered in waterflooding operations is the relatively poor sweep efficiency of the aqueous displacing medium; that is, the injected displacing medium tends to channel through certain portions of the reservoir as it travels from the injection system to the production system and to bypass other portions. Such poor sweep efficiency or macroscopic displacement efficiency may be due to a number of factors such as differences in the mobilities of the injected displacing liquids and the displaced reservoir oil and permeability variations within the reservoir which encourage preferential flow through some portions of the reservoir at the expense of other portions.

Various techniques have been proposed in order to improve the sweep efficiency of the injected displacing medium and thus avoid premature breakthrough at one or more of the wells comprising the production system. The most widely used procedure involves the addition of thickening agents to the injected displacing medium in order to increase the viscosity thereof and thus decrease its mobility to a value equal to or less then the mobility of the displaced reservoir oil, resulting in a "mobility ratio" of oil to water which is less than or equal to one. Many polymeric thickening agents including both anionic and cationic polyelectrolytes have been proposed for use in such mobility control operations. Thus, U.S. Pat. No. 3,085,063 discloses waterflooding in which the water is thickened by the addition of polyvinyl aromatic sulfonates such as sulfonated polystyrene and copolymers of such vinyl aromatic sulfonates. Similarly, U.S. Pat. No. 3,984,333 discloses waterflooding involving the injection of an aqueous solution thickened by block copolymers in which the water-soluble blocks are sulfonated polyvinylarenes and the relatively water-insoluble blocks are polymerized alpha olefins and/or hydrogenated dienes such as polyisoprene and polybutadiene. Synthetic anionic polymers such as those disclosed in the patents discussed above, as well as the more widely used partially hydrolyzed polyacrylamides, suffer a number of disadvantages in actual operations. Where the injected water or the reservoir water contains significant quantities of dissolved inorganic salts, their viscosity yield is decreased materially. Also U.S. Pat. No. 3,969,592 discloses water-soluble polymers manufactured by treating an aqueous suspension of protein with selected enzymes.

Also U.S. Pat. No. 4,110,232 discloses a waterflooding process for producing oil wherein an aqueous solution of a copolymer formed of hydrophobic olefinic segments and cationic aromatic segments is injected into oil-containing subterranean formation, and U.S. Pat. No. 4,222,881 discloses a waterflood oil recovery process involving the use of an amphoteric polyelectrolyte as a thickening agent for mobility control comprising a copolymer of a quaternary vinyl pyridinium sulfonate-styrene block copolymers.

During the drilling of an oil well, a usually aqueous fluid is injected into the well through the drill pipe and recirculated to the surface in the annular area between the well-bore wall and the drill string. The functions of the drilling fluid include: lubrication of the drill bit, transportation of cuttings to the surface, overbalancing formation pressure to prevent an influx of oil, gas or water into the well, maintenance of hole stability until casings can be set, suspension of solids when the fluid is not being circulated, and minimizing fluid loss into and possible associated damage/instability to the formation through which drilling is taking place.

Proper overbalancing of formation pressure is obtained by establishing fluid density at the desired level usually via the addition of barite (greater than or equal to 95% barium sulfate). Transportation of cuttings and their suspension when the fluid is not circulating is related to the fluid viscosity and thixotropy which depend on solids content and/or use of a polymer. Filter loss control is obtained also by the use of clays and/or added polymers.

Fluid properties are constantly monitored during the drilling operations and tailored to accommodate the nature of the formation stratum being encountered at the time. When drilling reaches the producing formation special concern is exercised. Preferentially low solids content fluids are used to minimize possible productivity loss by solids plugging. Proper fluid density for overbalancing formation pressure may be obtained by using high salt concentration aqueous brines while viscosity and filter loss control may be obtained by polymer addition. Substantial future oil well drilling will be at depths between 15 and 30 thousand feet where temperatures encountered can be 350° F. Temperatures such as these, coupled with the desire for low solids content and preferably no added solids, require brine tolerant and high temperature stable polymers for viscosity and filtration control. Conventionally employed polymers such as starch, carboxymethyl cellulose, and modified polyacrylates are not stable at the temperatures in question and some have severe brine tolerance limitations.

SUMMARY OF THE INVENTION

According to an aspect of the invention, there is provided a polymeric alkyl sulfonate salt of polyvinyl alcohol. More particularly, these sulfonate salts are of the formula

    H--R.sub.1 --H                                             (I)

wherein R₁ represents repeating polymeric units, said units consisting essentially of (i) units of the formula ##STR1## and (ii) units of the formula ##STR2## wherein: (a) R₂ --O is ethyleneoxy, propyleneoxy or mixtures thereof;

(b) n is zero or greater (e.g., 0-6), provided that (R₂ --O)_(n) has 18 or less carbon atoms;

(c) R₃ is a hydrocarbyl group having at least 2 carbon atoms; and

(d) M is a cation (preferably a monovalent cation).

R₂ may be CH₂ CH₂ or CH₂ CH₂ CH₂.

When R₂ --O represents mixtures of ethyleneoxy and propyleneoxy, R₂ --O may be, e.g., CH₂ CH₂ O--CH₂ CH₂ CH₂ O--CH₂ CH₂ O or CH₂ CH₂ CH₂ O--CH₂ CH₂ O--CH₂ CH₂ CH₂ O. It is expressly noted that polyvinyl alcohol may be derivatized with a series of reactants in less than stoichiometric amounts to form, in a single polyvinyl alcohol backbone chain, a variety of units each conforming to formula III. Thus, formula I is intended to connote a single polymer having, e.g., one or more of the following units in combination: ##STR3##

According to another aspect of the invention, there is provided a method for preparing a polymeric alkyl sulfonate salt comprising the steps of:

(i) reacting polyvinyl alcohol or polyvinyl alcohol having pendant polyalkyleneoxy segments with ClCH₂ CH═CH₂ in the presence of Na and DMSO in an amount sufficient to convert from about 5% to about 40% of the OH groups of said polyvinyl alcohol into groups of the formula --OCH₂ CH═CH₂ ; and

(ii) reacting said --OCH₂ CH═CH₂ groups of step (i) with NaHSO₃ in the presence of oxygen and water to convert said --OCH₂ CH═CH₂ groups into groups of the formula --OCH₂ CH₂ CH₂ SO₃ Na⁺.

According to another aspect of the invention, there is provided an aqueous fluid for use as either (a) a mobility control fluid in the secondary or tertiary recovery of oil or (b) a drilling fluid in the drilling of subterranean wells, said fluid having a salinity of at least 5 weight percent, said fluid comprising polymeric alkyl sulfonate salt according to formula (I) said polymeric alkyl sulfonate sals being present in an amount sufficient to thicken said fluid.

According to another aspect of the invention, there is provided an improved method for the recovery of oil from a subterranean oil reservoir penetrated by spaced injection and production systems in which an aqueous mobility control slug is introduced into said reservoir via said injection system to displace oil to said production system, the improvement comprising employing in said slug a thickening amount of one or more compounds according to formula (I).

According to another aspect of the invention, there is provided a method for maintaining the proper viscosity of an aqueous brine drill completion fluid used when drilling reaches a producing formation at a depth between 15 and 30 thousand feet, the temperature of said formation being more than about 325 degrees F., said method comprising incorporating in said fluid a viscosity increasing amount of one or more compounds according to formula (I).

DETAILED DESCRIPTION

The incorporation of from about 5 to 40 mer % of alkyl sulfonate groups, e.g., C₂ -C₆ alkyl sulfonate groups, particularly 3-propane sulfonate groups, onto the alcohol oxygens of polyvinyl alcohols imparts solubility to resulting polymers at high concentrations of salt and divalent ions.

As with all anionic polymers, the viscosity of aqueous solutions of these polymers falls with increasing salt content but, unlike other anionic polymers, at a salt concentration equivalent to about 10% w/v NaCl the viscosity begins to increase so that by about 20-25% salt the viscosity is as high or higher than in deionized water. The effect of rising salt is independent of the cation used with makes these polymers eminently suitable for enhanced oil recovery in reservoirs of higher brine content or for use in drilling fluids where high concentrations of calcium or other divalent ions may be present. The polymers are extremely stable both thermally and hydrolytically which also lends to their utility in the above-named processes.

The alkyl sulfonate salts according to the present invention may be prepared by a particular combination of process steps which may be carried out according to conventional technology. For example, a 3-propane sulfonate salt may be prepared according to the following reaction sequence: ##STR4##

In the above sequence, it is expressly noted that no stereochemical regularity is implied by the structures given. It is also noted that the number calculated by the formula, m/n×100, corresponds to the value for mer %.

Since polyvinyl alcohol is customarily made from the hydrolysis of polyvinyl acetate, it is likely that the polymeric alkyl sulfonate salt of formula (I) may contain units of the formula ##STR5##

The polymeric alkyl sulfonate salts of formula (I) may have a molecular weight of at least 25,000, e.g. from about 30,000 to about 500,000. It is contemplated that the higher molecular weight compounds made from super-high viscosity polyvinyl alcohols will have the most desirable thickening properties for mobility control fluids and drilling fluids.

In view of the compatibility of compositions used in the present invention with divalent metal ions, a preferred application of the invention is in reservoirs in which the connate water contains significant divalent ion concentrations and in situations where the available water for flooding or drilling contains divalent metal ions inconsistent with the use of conventional non-brine tolerant thickeners. Thus, a preferred application of the present invention is in those situations in which the reservoir waters and/or the waters employed in formulating the flooding medium or drilling fluid exhibit a divalent metal ion concentration of at least 0.1 weight percent. The invention is particularly useful where the reservoir, injection, and/or drilling waters have divalent metal ion concentrations of 0.5 weight percent or more. A similar consideration applies with regard to those situations in which the waters exhibit moderate to relatively high salinities even though the divalent metal ion concentration may be relatively low. Thus, another application of the invention is those situations in which the reservoir, injection and/or drilling waters have salinities of at least 5.0 weight percent, especially at least 10 weight percent, whether provided by monovalent salts such as sodium chloride or monovalent salts and divalent salts such as calcium or magnesium chloride.

The amount of formula (I) compound which may be used in accordance with aspects of the invention should be sufficient to achieve the desired thickening effect. For example, this compound may be added to water and injected into an oil-containing formation in a sufficient amount and concentration to effectively thicken the water so as to provide improved efficiency in driving the oil through the formation to the production well. This thickening agent may be added in concentrations so as to provide a graded viscosity at the trailing edge of the mobility control slug as disclosed in a paper by W. R. Foster entitled "A Low-Tension Waterflooding Process", Journal of Petroleum Technology, Vol. 25, February 1973, pp. 205-210, or graded viscosities at both the leading and trailing edges of the mobility control slug as disclosed in U.S. Pat. No. 4,018,281 to Chan. Alternatively, the thickening agent concentration may be relatively constant throughout. Normally, the viscosity of at least a portion of the mobility control slug should be at least as great as that of the reservoir oil and typically it will be within the range of about 1 to 4 times the viscosity of the reservoir oil.

Secondary oil recovery may be carried out utilizing injection and production systems as defined by any suitable arrangement of wells. One well arrangement commonly used in waterflooding operations and suitable for use in carrying out the present invention is an integrated five-spot pattern of the type illustrated in U.S. Pat. No. 3,927,716 to Burdyn et al. Other well arrangements may be used in carrying out aspects of the present invention, examples of which are set forth in the Burdyn et al patent. By the term "pore volume" as used herein is meant that volume of the portion of the formation underlying the well pattern employed, as described in greater detail in the Burdyn et al patent.

The mobility control slug may be injected in amounts ranging, e.g., from about 0.1 to about 1.0 pore volumes, more particularly, from about 0.25 to about 0.5 pore volumes.

EXAMPLE 1 Preparation of propyl sulfonate of polyvinyl alcohol

To a dry solution of 2 g (35.9 meq) 88% hydrolyzed poly(vinyl alcohol) (Aldrich, 125,000 Daltons) in 250 mL DMSO under Nitrogen were added 17 mL 0.66 M NaNp [i.e. sodium naphthenate; note H. Normant and B. Anzeol, Bull. Soc. Chem., France, (1960) 345.] in THF (11.2 meq) followed by 7.7 mL allyl chloride (94.4 mmole). After standing overnight at room temperature the DMSO was removed on a Kugelrohr, the residue dissolved in 100 mL of a 1:1 mixture of H₂ O and t-BuOH, stirred vigorously, and a solution of 2.12 g NaHSO₃ and a 1.59 g Na₂ SO₃ added in a minimum of water while air was passed through the flask at 10 mL/min. After 15 h 1.0 g NaOH were added, the mixture refluxed then neutralized with 5% HCl. Most of the t-BuOH was removed on a rotary evaporator and the residue dialyzed (Spectrapor Membrane, Arthur H. Thomas Co.) for two days. Filtration and evaporation gave 2.68 g (93-104%) pure product.

Viscosity Measurements

The viscosity of 1% solutions of 15-20 mer % and 30-40 mer % propane sulfonate derived from 125,000 Dalton poly(vinyl alcohol) in various brines were measured with a Canon size 100 viscometer. The 15-20 mer % propane sulfonate was prepared in accordance with Example 1. Flow times were about 90-220 sec. so that shear rates ranged from 580 to 1400 sec ⁻¹ [1.27×10⁵ ×flow time in sec=Shear rate; Note: J. R. VanWazer et al, "Viscosity and Flow Measurements, a Laboratory Handbook of Rheology", John Wiley, New York 1963].

Such shear rates are felt to be higher than expected for enhanced oil recovery flow and, consequently the viscosities measured are probably quite low compared to what they would be if measured at a lower shear. The results are tabulated in Table 1. The viscosities are promising in view of the low molecular weight and high shear rate.

                  TABLE 1                                                          ______________________________________                                          Viscosities in 1% Solution of Brine Tolerant Polymers                         A - 15-20% Propane Sulfonate                                                   B - 30-40% Propane Sulfonate                                                                  Viscosity in Centipoise                                         Salt Concentration                                                                              A        B                                                    ______________________________________                                         0        NaCl        2.24     2.28                                             1                    1.61     1.39                                             3                    1.39     1.29                                             7                    1.39     1.27                                             10                   1.58     1.35                                             15                   1.57     1.47                                             20                   1.86     1.62                                             30                   2.29     2.06                                             20       CaBr        1.59     --                                               40                   2.51     --                                               60                   3.53     Not                                                                            Soluble                                          ______________________________________                                    

The fairly large drop in viscosity from 0-1% salt is as expected for charged polymers. The increase in viscosity with further increase in salt was unexpected. Charged polymers either undergo a sudden conformational change to a tertiary structure of lowered hydrodynamic radius or a gradual monotonic collapse when salt level is increased. Polymers A and B on the other hand show an, as yet, unexplained increase in viscosity once the salt level has passed 4-8%.

For A and B part of the increase is due to the increase in viscosity of the salt solutions and would disappear if the viscosity were represented as specific viscosity, but most of the increase is real--and desirable.

Alghough the above absolute viscosities are relatively low, due to the low molecular weight (125,000) of the polymer used in these exploratory experiments, polymers of molecular weight 500,000 and 1.5 million would be expected to give higher viscosities.

In summary, polymers which can thicken aqueous brine have stability in enhanced oil recovery and in drilling fluids. In oil recovery, brine thickened by water can increase recovery because thickening water raises the viscous force to capillary force into which ratio limits the ultimate recovery in secondary waterflooding. In chemical waterflooding a thickened water slug helps maintain the integrity of the surfactant slug. In drilling fluids increased viscosity retards settling of cuttings.

The polymers currently available for these uses are either incapable of tolerating high brines (partially hydrolyzed polyacrylamides) or are not stable hydrolytically (polysaccharides). Consequently, it is desirable to find new polymers which can tolerate both high salt and high temperatures.

Poly (vinyl alcohol) has one hydroxyl group for every two carbons, but is not a very water soluble polymer. This is because its compact structure and many hydrogen bonds lead to a high crystal energy [T. H. Kwei in "Macromolecules, An Introduction to Polymer Science", (F. A. Bovey and F. H. Winslow, ed.) Academic Press, New York, 1979, pg. 273]. As little as 10% acetate side chains disrupts the crystals packing and makes the polymer water soluble, but not brine soluble. Incorporation of a modest number of propane sulfonate or pyrrolidinium sulfonate side chains was expected to give far higher water solubility because of the charged nature of those groups.

Charged polymers in water adopt extended conformations to minimize like charge repulsion at the expense of entropy. Higher salt concentrations increase shielding of charges from one another and the polymer contracts to minimize entropy. For example, converting poly (methacrylic acid) to its carboxylate salt by raising the pH gives a much more viscous solution because of chain extension [A. Oth and P. Doty, J. Phys. Chem., 56, 43 (1962)] but raising the NaCl level to as little as 0.5% NaCl results in substantial thinning of solutions of cationic poly (N-butyl-4-vinyl pyridine) [R. M. Fuoss, Disc. Faraday Soc., 11, 125 (1951)]. For simple linear polymers incapable of adopting complex tertiary structures viscosity loss with increasing salt level can be thought of as a loss of the "excess" chain extension of the charged polymer which just returns to the normal entropy determined level of extension of an uncharged polymer.

Particularly in view of this background, it was unexpected that, in contrast to other ionic polymers, viscosity of the polymers of the present invention increased with increasing salinity. 

What is claimed is:
 1. A polymeric alkyl sulfonate salt of the formula

    H--R.sub.1 --H                                             (I)

wherein R₁ represents repeating polymeric units, said units consisting essentially of (i) units of the formula ##STR6## and (ii) units of the formula ##STR7## having a mer % sufficient to impart enhanced brine solubility and thickening characteristics thereto wherein:(a) R₂ --O is ethyleneoxy, propyleneoxy or mixtures thereof; (b) n is zero or greater, provided that (R₂ --O)_(n) has 18 or less carbon atoms; (c) R₃ is a hydrocarbyl group having between 2 and 6 carbon atoms; and (d) M is a cation.
 2. A polymeric alkyl sulfonate salt according to claim 1, wherein R₂ is CH₂ CH₂ or CH₂ CH₂ CH₂ and n is 0-6.
 3. A polymeric alkyl sulfonate salt according to claim 1, wherein n is zero and M is a monovalent cation.
 4. A polymeric alkyl sulfonate salt according to claim 3, wherein said repeating polymeric units further contain units of the formula ##STR8##
 5. A polymeric alkyl sulfonate salt according to claim 3, wherein said repeating polymeric units consist essentially of from about 5% to about 40% of said units of formula (III) the remainder of said units being essentially of formula (II).
 6. A polymeric alkyl sulfonate salt according to claim 1 wherein said units of the formula (III) are of the formula ##STR9##
 7. A method for preparing the polymeric alkyl sulfonate salt according to claim 1 comprising the steps of:(i) reacting polyvinyl alcohol or polyvinyl alcohol having pendant polyalkyleneoxy segments with ClCH₂ CH═CH₂ in the presence of Na and DMSO in an amount sufficient to convert from about 5% to about 40% of the OH groups of said polyvinyl alcohol into groups of the formula OCH₂ CH═CH₂ and (ii) reacting said --OCH₂ CH═CH₂ groups of step (i) with NaHSO₃ in the presence of oxygen and water to convert said --OCH₂ CH═CH₂ groups into groups of the formula --OCH₂ CH₂ CH₂ SO₃ ⁻ Na⁺.
 8. A method according to claim 7, wherein polyvinyl alcohol is reacted according to said step (i).
 9. A polymeric alkyl sulfonate salt prepared according to claim 7 having approximately 21 mer % propane sulfonated polyvinyl alcohol. 